| Material Grade |
Alloy 601 / 625 N06600 / N06625, Alloy C276/N10276, Alloy B/UNS N10001, Alloy B-2/UNS N10665, Alloy B-3/UNS N10675, Alloy C22/UNS N06022,Alloy 800/N08800, Alloy 825/N08825, Alloy 400/N04400; etc |
| Outer Diameter |
3.18mm-101.60mm |
| Wall Thickness |
0.50mm-20.00mm |
| Length |
Normally fixed length 6m, can as per customer’s requirement |
| Standard |
ASTM B163; ASTM B167; ASTM B444; ASTM B622 etc. |
Alloy 601 Chemical composition
| % |
Ni |
Cr |
Fe |
C |
Mn |
Si |
S |
Al |
Cu |
| min |
58.0 |
21.0 |
balance |
|
|
|
|
1.00 |
|
| max |
63.0 |
25.0 |
0.10 |
1.00 |
0.50 |
0.015 |
1.70 |
1.00 |
Alloy 625 Chemical composition
| % |
Ni |
Cr |
Mo |
Fe |
C |
Mn |
Si |
P |
S |
Co |
Nb+Ta |
Al |
Ti |
| min |
58.0 |
20.0 |
8.0 |
|
|
|
|
|
|
|
3.15 |
|
|
| max |
|
23.0 |
10.0 |
5.0 |
0.10 |
0.50 |
0.50 |
0.015 |
0.015 |
1.00 |
4.15 |
0.40 |
0.40 |
Features: Alloy 601 has good resistance to heat and corrosion, especially outstanding to oxidation at elevated temperatures up to 1200℃. It also has high strength, good fabricability and good resistance to aqueous corrosion.
Applications: Chemical process industry, waste incinerators, power generation equipment, heat treating equipment, and gas turbine engine components.
Features: Alloy 625 has excellent strength at temperatures up to 816℃. At higher temperatures, its strength is generally lower than that of other solid solution strengthened alloys. Alloy 625 has good oxidation resistance at temperatures up to 980℃ and shows good resistance to aqueous corrosion, but is relatively moderate compared to other more capable corrosion resistant alloys.
Applications: Chemical process industry and sea water application. Alloy 625 is used in short term applications at temperatures up to 816℃. For long term service, it is best restricted to a maximum of 593℃, because long term exposure above 593℃ will result in significant embrittlement.